MIM 4605 (Quenched & Tempered, High Hardness) for Metal Injection Molding Process Services
MIM 4605 (Quenched & Tempered, High Hardness) for Metal Injection Molding Process Services
Share
MIM 4605 is a premium material that has been quenched and tempered to achieve high hardness, making it ideal for metal injection molding process services. Its superior strength and durability provide top-notch performance, ensuring the success of your projects. Trust MIM 4605 for all your metal injection molding needs.
Low-Alloy Steel
Iron-based alloys, also known as low-alloy steels, are often used in structural applications because of their high hardness and performance strength.
MIM-4605
MIM 4605 has excellent strength and good ductility through the MIM process, and has a wide range of applications in the automotive, consumer goods and hand tool industries.
MIM-4605 Ingredients
|
MIM-4605 |
iron |
silicon |
carbon |
nickel |
molybdenum |
|
weight percentage |
BaL. |
1.00 |
0.40-0.60 |
1.50-2.50 |
0.20-0.50 |
MIM-4605 Mechanical Properties
|
Material |
density |
tensile strength |
Yield strength (0.2%) |
Impact strength |
hardness |
Elongation (within %25.4mm) |
|
MIM-4605 |
≥7.50g/cm3 |
≥600Mpa |
≥400Mpa |
70J |
≥90 HV10 |
≥5% |
The alloy can be quenched and tempered heat treated to obtain a variety of strengths and wear resistance properties. Generally, we can produce the following low and high hardness special types:
MIM-4605 Low Hardness Mechanical Properties
|
Material |
density |
tensile strength |
Yield strength (0.2%) |
Impact strength |
hardness |
Elongation (within %25.4mm) |
|
MIM-4605 |
≥7.5g/cm3 |
1151Mpa |
1034Mpa |
38J |
36 HRC |
≥3% |
MIM-4605 High Hardness Mechanical Properties
|
Material |
density |
tensile strength |
Yield strength (0.2%) |
Impact strength |
hardness |
Elongation (within %25.4mm) |
|
MIM-4605 |
≥7.5g/cm3 |
1655Mpa |
1480Mpa |
55J |
48 HRC |
≥2% |